Researchers at the Centre de Nanosciences et de Nanotechnologies (C2N), in collaboration in particular with researchers at the German Fraunhofer ISE, have succeeded to trap sunlight efficiently in a solar cell thanks to an ultrathin absorbing layer made of 205 nm-thick GaAs on a nanostructured back mirror. With this new architecture, an efficiency of nearly 20% was obtained
Up to now, the laboratory state-of-the-art 20%-efficient solar cells required at least 1 micrometer-thick layers of semiconductor material (GaAs, CdTe or copper indium gallium selenide -CIGS-), or even 40 µm or more in the case of silicon. A significant thickness reduction would enable material savings of scarce materials like Tellerium or Indium and industrial throughput improvements due to shorter deposition times. However, thinning absorber automatically reduces absorption of sunlight and conversion efficiency. A flat mirror at the backside of the cell can help and lead to double-pass absorption, but no more. Previous attempts of light trapping have been greatly limited in performance by the optical and electrical losses.
Researchers of the team led by Stéphane Collin and Andrea Cattoni at the Centre de Nanosciences et de Nanotechnologies - C2N (CNRS/University Paris-Saclay), in collaboration in particular with the Fraunhofer ISE, have developed a new strategy to trap light in ultrathin layers made of only 205 nm-thick gallium arsenide, a semiconductor of the III-V family. The guiding idea has been to conceive a nanostructured back mirror to create multiple overlapping resonances in the solar cell, identified as Fabry–Perot and guided-mode resonances. They constrain light to stay longer in the absorber, resulting in efficient optical absorption despite the low quantity of material. Thanks to numerous resonances, absorption is enhanced over a large spectral range that fits the solar spectrum from the visible to the infrared. Controling the fabrication of patterned mirrors at the nanometer scale has been a key aspect of the project. The team used nanoimprint lithography to directly emboss directly a sol-gel derived film of titanium dioxide, an inexpensive, rapid and scalable technique.
Can ultrathin solar cells be further improved? The work published in Nature Energy demonstrates that this architecture should enable 25% efficiency in the short term. Even if the limits are still unknown, researchers are convinced that the thickness could be further reduced without efficiency loss, at least by a factor of two. GaAs solar cells are still commercially limited to space application due to their cost. However, researchers are already working on how to extend this concept for large-scale photovoltaics made of CdTe, CIGS or silicon materials.
A 19.9%-efficient ultrathin solar cell based on a 205-nm-thick GaAs absorber and a silver nanostructured back mirror,
Hung-Ling Chen1, Andrea Cattoni1, Romaric De Lépinau1,2, Alexandre W. Walker 3, Oliver Höhn3, David Lackner3, Gerald Siefer3, Marco Faustini4, Nicolas Vandamme1, Julie Goffard1,2, Benoît Behaghel1, Christophe Dupuis1, Nathalie Bardou1, Frank Dimroth3 & Stéphane Collin1,2
Nature Energy (2019)
1 Centre de Nanosciences et de Nanotechnologies - C2N (CNRS / University Paris-Sud/Paris-Saclay)
2 Institut Photovoltaïque d’Ile-de-France (IPVF)
3 Fraunhofer Institute for Solar Energy Systems (ISE)
4 Laboratoire Chimie de la Matière Condensée de Paris – LCMCP (Sorbonne Université / CNRS / Collège de France)
- Stéphane Collin, CNRS Researcher at C2N
- Andrea Cattoni, CNRS Researcher at C2N
Figure: (left) Sketch of an ultrathin solar cell made of GaAs with a nanostructured back mirror. (right) Photograph of a sample showing the diffraction effect of a nanostructured mirror in air (colored shine) and the absorption enhancement effect in ultrathin solar cells (square black areas). Copyright C2N.